Base oil SAE 10/95
Specification
|
|
|
|
Value |
|
|
|
Requirements |
Units |
Minimum |
Maximum |
Typical |
Testing methods |
|
Appearance in temperature of 20oC |
- |
|
|
transparent, without any suspension |
visual
|
|
Structural viscosity in the temp. of -20oC |
mPa.s |
|
|
2600 |
PN-88C/04150 |
|
Kinetic viscosity in the temp. of100oC not lower than |
mm2/s |
5,2 |
5,9 |
5,52 |
PN-EN ISO3104 ASTM D 445 |
|
Kinetic viscosity in the temp. of40oC |
mm2/s |
|
|
34 |
PN-EN ISO3104 ASTM D 445 |
|
Viscosity index not lower than |
- |
95 |
|
96 |
PN-79/C04013 ASTM D 2270 |
|
Flow temperature not higher than |
oC |
|
-15 |
-15 |
ASTM D 5950 ASTM D 5985 ASTM D 97 |
|
The ignition temperature not lower than |
oC |
210 |
|
230 |
PN EN ISO 2592 ASTM D 92 |
|
Residue after coking not higher than |
%(m/m) |
|
0,03 |
no |
PN EN ISO 10370 ASTM D 4530 |
|
The acid value not higher than |
mgKOH/g |
|
0,05 |
0,014 |
PN-88/C04049 |
|
Residue after incineration not more than |
%(m/m) |
|
0,005 |
no |
PN EN ISO 6245 ASTM D 482 |
|
Water content |
%(m/m) |
|
|
no |
PN EN ISO 12937 ASTM D 6304 |
|
Corroding action in temp. of100oC in 3h time, on copper plates |
Corrosion ratio |
|
1 |
1 |
PN EN ISO 2160 ASTM D 130 |
|
Volatile matter content by Noack’s method |
%(m/m) |
|
15 |
11 |
PN-C-04124:2000 DIN 51581 |
|
Foaming resistance Foaming propensity:
Foam stability:
|
ml ml ml
ml ml ml |
|
|
250 25 250
0 0 0 |
PN-85/C04055 |
|
Colour not higher than |
Standard number |
|
1 |
0,5 |
PN-80/C-04034 ASTM D 1500 |
|
Density in the temp. of15oC |
g/cm3 |
|
|
0,864 |
PN EN ISO 12185 ASTM D 4052 |